Strength + Thin Margins
HASS reports 460 MPa biaxial flexural strength, while the material's microstructure helps support thin restoration margins with reduced chipping.
Double click image to zoom in
Click image to open expanded view
HASS · LITHIUM DISILICATE PRESS INGOT
Controlled Translucency.
Reliable Pressing.
Amber Press is a lithium disilicate press ingot developed for stable pressing, high esthetics and efficient laboratory processing. Its crystallised cross-linked microstructure supports thin margins, reduced chipping and minimal reaction layer after pressing. The LT range provides lower translucency for staining and cut-back workflows where additional masking is beneficial.
460 MPaBiaxial Flexural Strength
LowReaction Layer After Pressing
0Acid Clean-Up Step Required*
LTSelected Optical Family
*HASS states that Amber Press leaves minimal reaction layer and does not require acid liquid for clean-up when processed according to the manufacturer's workflow. Always follow the current IFU.
WHY AMBER PRESS
Designed for the Press Lab.
Amber Press combines the familiar lost-wax pressing technique with a lithium disilicate material engineered for strength, edge stability and cleaner post-press processing.
Minimal Reaction Layer
Amber Press is engineered to leave very little reaction layer after pressing, simplifying divesting and post-press clean-up.
Natural Esthetics
Multiple translucency and opacity options support staining, cut-back and layering approaches across a broad range of restorative cases.
SELECTED TRANSLUCENCY
LT · Balanced Masking for Staining and Cut-Back.
LT
Low Translucency
LT provides lower translucency than HT, helping balance masking and vitality in staining and cut-back workflows.
Lower TranslucencyProvides greater masking than HT while retaining natural esthetic potential.
Staining / Cut-BackHASS positions LT for staining and cut-back workflows with compatible finishing ceramics.
Balanced Optical ControlUseful when the case needs more control over the underlying colour without moving to a dedicated MO layering framework.
INDICATIONS
One Press System. Broad Restorative Coverage.
Amber Press is indicated for a range of lithium disilicate restorations. Follow the current HASS IFU for design, minimum thickness, connector dimensions and case selection.
Veneers
Inlays
Onlays
Anterior Crowns
Posterior Crowns
3-Unit Bridges*
*Manufacturer documentation lists 3-unit bridges with posterior extension limited to the second premolar. Confirm the current IFU before case selection.
PRESS WORKFLOW
From Wax Pattern to Final Ceramic.
Amber Press is designed around the conventional lost-wax pressing technique used in dental laboratories.
01Wax-Up
02Sprue
03Invest
04Burnout
05Press
06Divest
07Stain / Cut-Back & Finish
CLEANER POST-PRESS PROCESSING
Less Reaction Layer. Less Clean-Up.
One of Amber Press's strongest laboratory advantages is what happens after pressing.
Minimal Reaction Layer
HASS states that Amber Press leaves only a small amount of reaction layer after pressing, helping simplify post-press processing and reduce unnecessary adjustment.
No Acid Liquid Required
According to HASS, acid liquid is not required for reaction-layer clean-up in the recommended Amber Press workflow, supporting a simpler and less hazardous laboratory process.
VENEERING FLEXIBILITY
Work With Familiar Ceramic Systems.
Amber Press is compatible with a range of veneering materials intended for lithium disilicate restorations. HASS also publishes specific guidance for selected zirconia veneering porcelains when used with Amber Press.
Lithium Disilicate VeneeringStainingCut-BackLayering
Upload Amber Press layering / veneering image in Theme Customize
REAL RESTORATIONS
Press for Strength. Finish for Esthetics.
Use HASS or DDA-approved cases to show the final optical result, margin quality and the difference between monolithic, cut-back and layered techniques.
Upload Amber Press anterior case
Anterior Esthetics
Show natural contour, translucency and surface character in highly visible anterior restorations.
Upload Amber Press layered / cut-back case
Cut-Back & Characterisation
Demonstrate how pressed lithium disilicate can be refined with cut-back, stain and glaze techniques.
Upload Amber Press posterior case
Posterior Restorations
Show practical laboratory results for inlays, onlays and posterior crowns within the manufacturer's indication and design requirements.
PRESS OR MILL?
Amber Press vs Amber Mill
Both use HASS lithium disilicate technology, but the production workflow is fundamentally different.
| Feature | Amber Press | Amber Mill |
|---|---|---|
| Manufacturing Method | Lost-wax press technique | CAD/CAM milling |
| Best Fit | Laboratories using wax-up, investment and ceramic pressing workflows | Digital CAD/CAM laboratories and clinics |
| Reported Strength | 460 MPa biaxial flexural strength | Approx. 450 MPa fully crystallised |
| Optical Selection | Dedicated HT, LT and MO ingot families | Heat-treatment-based translucency control across HT+, HT, MT, LT and MO |
| Finishing Approach | HT/LT: staining and cut-back oriented | Crystallisation followed by polish, stain and/or glaze according to the selected protocol |
| Key Workflow Advantage | Minimal reaction layer and no acid clean-up requirement in the recommended workflow | Digital design, milling and adjustable translucency |
TECHNICAL INFORMATION
Amber Press LT Specifications
| Material | Lithium disilicate-based press ingot |
|---|---|
| Product Family | Amber Press |
| Selected Translucency | LT · Low Translucency |
| Reported Biaxial Flexural Strength | 460 MPa |
| Primary Technique | Staining / cut-back workflow |
| Reaction Layer | Minimal after pressing according to HASS |
| Acid Clean-Up | Not required in the manufacturer's recommended Amber Press workflow |
| Indications | Veneers, inlays, onlays, anterior single crowns, posterior single crowns and manufacturer-specified 3-unit bridges. Always follow the current HASS IFU. |
| Compatible Processing | Use appropriate lithium disilicate investment, press furnace settings and HASS pressing schedules for the selected furnace. |
Manufacturer-reported physical-property and workflow data. Pressing results depend on investment, furnace calibration, pressing parameters, restoration design and finishing procedure. Refer to the current HASS Instructions for Use and pressing schedule for your furnace before clinical use.
FREQUENTLY ASKED QUESTIONS
Amber Press Workflow Questions
What is the difference between Amber Press HT, LT and MO?
HT is the more translucent option, LT provides increased masking, and MO is the more opaque framework-oriented option. HASS positions HT and LT primarily for staining / cut-back workflows and MO for layering.
Does Amber Press require acid reaction-layer removal?
HASS states that Amber Press produces only a small reaction layer and does not require acid liquid for clean-up when processed according to the recommended workflow.
Can Amber Press be layered with veneering ceramic?
Yes. HASS documents compatibility with multiple veneering systems. Always confirm the current HASS guideline and the veneering ceramic manufacturer's instructions before use.
Is Amber Press the same material as Amber Mill?
They are both lithium disilicate-based HASS restorative materials, but Amber Press is processed by the lost-wax press technique, while Amber Mill is a CAD/CAM material designed for milling and subsequent crystallisation.
PRESS CERAMIC SUPPORT FROM DDA
Need Help With Your Lithium Disilicate Press Workflow?
Dental Dynamics Australia supports dental laboratories with pressable ceramics, furnaces, investment materials and practical ceramic workflows. Talk to our team about Amber Press selection, furnace compatibility, pressing schedules and finishing techniques.
Talk to a DDA Expert